چکیده مقاله
Due to the low wear resistance of the as cast ductile iron DI , it is thought to apply a developed austempering heat treatment process defined by two step austempering process that enhance the mechanical properties as well as the wear property In this study two DI alloys were used, the first one was unalloyed DI and the second contains 0 2% Cr Two batches of samples were prepared for each alloy The first batch was proceed by conventional single step austempering treatment, where the samples were austenitized at 900 °C for 1 hour and then quenched in a salt bath at austempering temperature of 360 °C for 1 hour A developed austempering process or two step austempering process was applied on the second batch of samples The samples were austenitized at 900 °C for 1 hour and then quenched consequently at 360 °C and while being kept at that temperature, the temperature of the salt bath was raised by 29 °C in 1 hour So, the final austempering temperature reached 389 °C and then cooled directly by forced air The correlation between microstructure, mechanical properties, as well as abrasion resistance has been done for both conventional single step and two step ADIs The two step or developed ADI achieved superior abrasion resistance than the conventional one This marked improvement in abrasion resistance of the two step ADI is attributed to the high amount of transformed fine ausferrite in the final structure The wear mechanisms were also defined by means of studying the worn surface using scanning electronic microscope
کلیدواژهها
نویسندگان
Khaled M. Ibrahim
CMRDI, Cairo Egypt
Ahmed Elsawy
TTU, Tennesse, USA
شیوه ارجاع
Ibrahim, Khaled M. and Elsawy, Ahmed,1384,Enhancement abrasion resistance of ductile cast iron by applying two-step austempering process,01st Tehran International Congress on Manufacturing Engineering (TICME2005),Tehran
ارائهشده در
مجموعه مقالات اولین کنفرانس بین المللی و هفتمین کنفرانس ملی مهندسی ساخت و تولید1 فروردین 1384 · تهران