In the present work, API 5L X70 HSLA steel plates were uniformly preheated at different temperatures before the welding process SMAW E7010, E8018 and E7024 electrodes are used to weld the butt joint of API 5L X70 steel plates with 20mm thickness Tensile and Charpy impact tests were performed on the samples according to AWS and ASTM standards The results show that by increasing the preheat temperature, tensile strength of the HAZ was decreased and the impact energy was increased This behavior in mechanical properties of the HAZ is due to the stress relief along with the microstructural modification of HAZ
کلیدواژهها
نویسندگان
m Ghaderi
Post graduate Student, Department ofMaterials Engineering, KarajBranch,Islamic Azad University,Karaj, Iran
h Sabet
Associate Professor, Department of Materials Engineering,KarajBranch, Islamic Azad University, Karaj, Iran
h Ahmad Mehrabi
Assistant Professor, Department of Materials Engineering,KarajBranch, Islamic Azad University, Karaj, Iran
شیوه ارجاع
Ghaderi, m and Sabet, h and Ahmad Mehrabi, h,1395,Influence of preheat temperature on the impact energy and tensile properties of the HSLA-70 steel,The second international conference on welding and non-destructive testing, the 17th national conference on welding and inspection, and the sixth national conference on non-destructive testing,Isfahan
ارائهشده در
مجموعه مقالات دومین کنفرانس بین المللی جوشکاری و آزمایش های غیرمخرب، هفدهمین کنفرانس ملی جوش و بازرسی و ششمین کنفرانس ملی آزمایش های غیرمخرب30 آذر 1395 · اصفهان