Al 1050 and Al 3105 aluminum alloy sheets were joined via ultrasonic spot welding USW Due to mechanical and thermal cycles during USW, both diffusion and mechanical mixing facilitated the formation of welded interfaces The alloying element, Mn, in Al 3105 diffused into Al 1050 during USW, and diffusion behavior varied with selection of top sheet The fracture mechanism during lap shear testing, i e debonding or pullout fracture, varied based on welding power, time and pressure
کلیدواژهها
نویسندگان
Hamidreza Masoumi
Master of Science ,Golpayegan university of technology, Iran
Amirhossein Meysami
FacultyMember, Golpayegan university of technology, Iran
Hamed Razavi
FacultyMember, Golpayegan university of technology
Mohammad Khodaei
FacultyMember, Golpayegan university of technology , Iran
شیوه ارجاع
Masoumi, Hamidreza and Meysami, Amirhossein and Razavi, Hamed and Khodaei, Mohammad,1399,The effects of welding parameters on ultrasonic spot welding of dissimilar Al 3105 and Al 1050 alloys,3rd International Conference on Welding and Non-Destructive Testing of Iran, 21st National Conference on Welding and Inspection and 10th National Conference on Non-Destructive Testing,Isfahan
ارائهشده در
مجموعه مقالات سومین کنفرانس بین المللی جوشکاری و آزمایش های غیرمخرب ایران، بیست و یکمین کنفرانس ملی جوش و بازرسی و دهمین کنفرانس ملی آزمایش های غیرمخرب13 اسفند 1399 · اصفهان