Dissimilar welding of Inconel 625 superalloy IN 625 to AISI 316L austenitic stainless steel SS 316L by using 25 μm thick AWS BNi3 nickel base interlayer and transient liquid phase TLP bonding was carried out and the structure and mechanical properties of bonded specimens was examined TLP bonding was performed at 1050 1250°C temperature range for 5 20min under the shielding of argon atmosphere The microstructural and mechanical evaluations revealed that the increasing of bonding temperature and time result in out diffusion of melting point reducing elements from bonding zone and progresses of isothermal solidification The increasing of temperature from 1050°C to 1150°C and bonding time up to 20min caused completion of isothermalsolidification and significant increasing of shear strength of bonded specimens
کلیدواژهها
نویسندگان
M.J Baghban
M MosallaeeH HajisafariA Babanejad
M Mosallaee
M.J BaghbanH HajisafariA Babanejad
H Hajisafari
M.J BaghbanM MosallaeeA Babanejad
A Babanejad
M.J BaghbanM MosallaeeH Hajisafari
شیوه ارجاع
Baghban, M.J and Mosallaee, M and Hajisafari, H and Babanejad, A,1400,Evaluation of dissimilar IN-625/SS-316L joint welded by using transient liquid phase bonding method,4th International Conference on Welding and Non Destructive Testing & 22nd National Conference on Welding & Inspection & 11th National Conference on NDT,Isfahan
ارائهشده در
مجموعه مقالات چهارمین کنفرانس بین المللی جوشکاری و آزمایش های غیرمخرب و بیست و دومین کنفرانس ملی جوش و بازرسی و یازدهمین کنفرانس ملی آزمایش های غیرمخرب18 اسفند 1400 · اصفهان