Stainless steels and titanium based alloys are among the engineering materials that have become very popular among craftsmen and researchers due to their excellent corrosion resistance, weldability and other properties The integration of titanium and stainless steel alloys is also widely used in many industries Therefore, in this study, the effect of temperature on the dissimilar joining of Ti6Al4V alloy and 304 AISI stainless steel through the transient liquid phase has been investigated The process was performed at three temperatures of 900, 950 and 1000 °C and a fixed time of 60 minutes A scanning electron microscope equipped with Energy Dispersive Spectroscopy analysis was used to examine the junction area In none of the samples was the isothermal solidification zone completely formed The shear strength test also showed that with increasing temperature, the shear strength decreased Thus, the highest shear strength was obtained at 900 °C Xray diffraction patterns confirm the presence of intermetallic compounds based on iron, copper and titanium
کلیدواژهها
نویسندگان
Iman Aghaei
Master of science, Isfahan University of Technology, Iran
Morteza Shamanian
Professor, Isfahan University of Technology, Iran
Abbas Bahrami
Professor, Isfahan University of Technology, Iran
Mohmmad Amin Mokhtari
Assistant professor, Isfahan University of Technology, Iran
شیوه ارجاع
Aghaei, Iman and Shamanian, Morteza and Bahrami, Abbas and Mokhtari, Mohmmad Amin,1400,Evaluation of properties of dissimilar joints of Ti–6Al–4V to AISI 304 austenitic stainless steel by transient liquid phase method,4th International Conference on Welding and Non Destructive Testing & 22nd National Conference on Welding & Inspection & 11th National Conference on NDT,Isfahan
ارائهشده در
مجموعه مقالات چهارمین کنفرانس بین المللی جوشکاری و آزمایش های غیرمخرب و بیست و دومین کنفرانس ملی جوش و بازرسی و یازدهمین کنفرانس ملی آزمایش های غیرمخرب18 اسفند 1400 · اصفهان