چکیده مقاله
In this study, the diffusion bonding of Zr702 alloy to A516 low alloy steel was performed using multi interlayers diffusion bonding was performed by SPDB method using spark plasma sintering technique SPS at temperatures of 900 ⁰C and time of 30 minutes In order to study the microstructure of the interfaces in different joints, a field emission electron microscope FESEM equipped with an EDS analyzer was used The results showed that diffusion was well done in the interface of the interlayers Nb Ti solid solution was formed at the Ti/Nb interface that two areas α β Ti acicular shaped zone I and β Ti,Nb zone Ⅱ are visible The Ti/Nb interface is free from any intermetallic, crack and Discontinuity Also, the thickness of the mentioned areas I & Ⅱ was measured at 1 525 microns in zone I and 8 390 microns in zone 1, respectively
کلیدواژهها
نویسندگان
Ali Pourjafar
PhD candidate, Department of Materials Science & Engineering, Faculty of Engineering, Shahid Chamran University of Ahvaz, Ahvaz, Iran
Reza Dehmolaei
Assistant Professor, Department of Materials Science & Engineering, Faculty of Engineering, Shahid Chamran University of Ahvaz, Ahvaz, Iran
Seyed Reza Alavi Zare
Assistant Professor, Department of Materials Science & Engineering, Faculty of Engineering, Shahid Chamran University of Ahvaz, Ahvaz, Iran
شیوه ارجاع
Pourjafar, Ali and Dehmolaei, Reza and Alavi Zare, Seyed Reza,1400,Microstructural investigation of titanium-niobium interlayer diffusion bonding in Zr702 to A516 carbon steel,4th International Conference on Welding and Non Destructive Testing & 22nd National Conference on Welding & Inspection & 11th National Conference on NDT,Isfahan
ارائهشده در
مجموعه مقالات چهارمین کنفرانس بین المللی جوشکاری و آزمایش های غیرمخرب و بیست و دومین کنفرانس ملی جوش و بازرسی و یازدهمین کنفرانس ملی آزمایش های غیرمخرب18 اسفند 1400 · اصفهان