چکیده مقاله
Hydroxyapatite is a calcium phosphate that is a very important ceramic applicable in biomaterials Nano hydroxyapatite has been considered as a biological material for the use in body implants due to its similarity in size, crystallography and chemical composition with human hard tissues In this research, hydroxyapatite was produced by combustion synthesis method and then it PLA/HA composites were manufactured via 3D printing method Hydroxyapatite nanoparticles were prepared using calcium nitrate, ammonium phosphate, urea and nitric acid In the continuation of the research, XRD was used to evaluate the phase structure of the produced hydroxyapatite and biodegradability test was also taken from PLA 10 wt% HA compounds From the FTIR analysis, the presence of carbonyl and phosphate groups in the PLA/HA composite were confirmed
کلیدواژهها
نویسندگان
Samaneh Jahanbazi
Materials Engineering Group, Golpayegan College of Engineering, Isfahan University of Technology,Golpayegan ۸۷۷۱۷ ۶۷۴۹۸, Iran
Seyed Mahdi Rafiaei
Materials Engineering Group, Golpayegan College of Engineering, Isfahan University of Technology,Golpayegan ۸۷۷۱۷ ۶۷۴۹۸, Iran
شیوه ارجاع
Jahanbazi, Samaneh and Rafiaei, Seyed Mahdi,1402,Fabrication of PLA based composites through the employment of 3D printing for biological applications,6th International Conference on Welding and Non Destructive Testing & 24th National Conference on Welding & Inspection & 13th National Conference on NDT & 2nd National Conference on Additive Manufacturing,Tabriz
ارائهشده در
مجموعه مقالات ششمین کنفرانس بین المللی جوشکاری و آزمایش های غیرمخرب، بیست و چهارمین کنفرانس ملی جوش و بازرسی، سیزدهمین کنفرانس ملی آزمایش های غیرمخرب و دومین کنفرانس ملی ساخت افزایشی2 اسفند 1402 · تبریز