Nowadays, with the widespread use of additive manufacturing applications, it hasbecome important to join the parts obtained from this production method with othermaterials In this study, it was aimed to investigate whether the AlSi10Mg alloyproduced by additive manufacturing can be joined to the AA5083 alloy, which is widelyused in industrial applications, by friction stir welding FSW method In this context,sheets produced in dimensions of 200x50x4 mm3 were used FSW was performed usinga tool with triangular pyramid geometry with a rotation speed of 800 rpm, at a traversespeed of 85 mm x min 1, and a pressure force of 7 kN The tilt angle of the FSW toolwas kept constant at 2° FSW was performed using X40CrMoV5 1 1 2344 hot worktool steel consisting of a shoulder with a diameter of 18mm and a 24° cone angle Afterthe FSW, the specimens were taken from the joint areas to investigate the structural andmechanical properties It is observed that a very fine grained structure emerges in themixing region The tension test specimens were taken from the FSW zone parallel to thewelding direction by wire electron discharge machine EDM Tensile tests wereperformed using the shape of a dog bone specimen which in accordance with the ASTME8 The tests were carried out using a tensile tester at a 1x10 3 s 1 strain rate Evaluations were performed by comparing the findings with the base materials
کلیدواژهها
نویسندگان
Tevfik Küçükömeroğlua
Karadeniz Technical University, Faculty of Engineering, Department of Mechanical Engineering, ۶۱۰۸۰Trabzon, Turkey
Serkan Karakaşa
Tevfik Küçükömeroğlua Karadeniz Technical University, Faculty of Engineering, Department of Mechanical Engineering, ۶۱۰۸۰Trabzon, TurkeyYaşar SertaHüccet KahramanzadeaGürel Çamb
Yaşar Serta
Tevfik Küçükömeroğlua Karadeniz Technical University, Faculty of Engineering, Department of Mechanical Engineering, ۶۱۰۸۰Trabzon, TurkeySerkan KarakaşaHüccet KahramanzadeaGürel Çamb
Hüccet Kahramanzadea
Tevfik Küçükömeroğlua Karadeniz Technical University, Faculty of Engineering, Department of Mechanical Engineering, ۶۱۰۸۰Trabzon, TurkeySerkan KarakaşaYaşar SertaGürel Çamb
Gürel Çamb
Tevfik Küçükömeroğlua Karadeniz Technical University, Faculty of Engineering, Department of Mechanical Engineering, ۶۱۰۸۰Trabzon, TurkeySerkan KarakaşaYaşar SertaHüccet Kahramanzadea
شیوه ارجاع
Küçükömeroğlua, Tevfik and Karakaşa, Serkan and Serta, Yaşar and Kahramanzadea, Hüccet and Çamb, Gürel,1402,Welding of AlSi10Mg Alloy Produced by Additive ManufacturingMethod to AA5083 Alloy by Friction Stir and Mechanical PropertiesInvestigation,6th International Conference on Welding and Non Destructive Testing & 24th National Conference on Welding & Inspection & 13th National Conference on NDT & 2nd National Conference on Additive Manufacturing,Tabriz
ارائهشده در
مجموعه مقالات ششمین کنفرانس بین المللی جوشکاری و آزمایش های غیرمخرب، بیست و چهارمین کنفرانس ملی جوش و بازرسی، سیزدهمین کنفرانس ملی آزمایش های غیرمخرب و دومین کنفرانس ملی ساخت افزایشی2 اسفند 1402 · تبریز