چکیده مقاله
In this study, dissimilar transient liquid phase bonding of SAF 2205 and IN X 750 alloys was investigated The joining process was carried out at 1100 °C for different bondingtimes of 1, 15, and 30 min with BNi 3 interlayer Characterization of the bonded samples was performed using optical microscopy and scanning electron microscopy equippedwith energy dispersive X ray spectroscopy and electron backscatter diffraction technique In addition, microhardness and shear strength tests were done to measure themechanical properties The results of microstructural studies showed that due to the bonding process, several zones with different microstructures have been created in thebonding region The width of these zones depended on the holding time of the process The results of EBSD studies showed that different phases such as BN, Ni3B, CrB, Cr2Band Ni2Si were formed in the bonding area Isothermal solidification was completed in 30 min The results of microhardness test in the joint area also showed that the maximum hardness was about 850 HV, which had belonged to the athermally solidified zone The maximum shear strength was about 465 MPa, which had belonged to the bonded sample with complete isothermal solidification The fracture mechanism also changed due to the microstructure difference of the samples from brittle fracture in samples with athermal solidification structure to ductile fracture in samples without athermal solidification zone The results obtained from the simulation of residual stresses showed that the maximum difference in residual stresses was between athermal solidification and isothermal solidification zones, which could increase the possibility of nucleation and propagation of cracks in the interface of these zones
کلیدواژهها
نویسندگان
Ehsan Baharzadeh
Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran
Morteza Shamanian
Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran
Mahdi Rafiei
Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch,Islamic Azad University, Najafabad, Iran
Hossein Mostaan
Faculty of Engineering, Department of Materials and Metallurgical Engineering, Arak University, Arak, Iran
شیوه ارجاع
Baharzadeh, Ehsan and Shamanian, Morteza and Rafiei, Mahdi and Mostaan, Hossein,1399,EBSD Study and simulation of residual stresses in dissimilar transient liquid phase joining of SAF 2205 duplex stainless steel to,3rd International Conference on Welding and Non-Destructive Testing of Iran, 21st National Conference on Welding and Inspection and 10th National Conference on Non-Destructive Testing,Isfahan
ارائهشده در
مجموعه مقالات سومین کنفرانس بین المللی جوشکاری و آزمایش های غیرمخرب ایران، بیست و یکمین کنفرانس ملی جوش و بازرسی و دهمین کنفرانس ملی آزمایش های غیرمخرب13 اسفند 1399 · اصفهان