This research was carried out to numerically calculate the amount of hydrogen in pre heated and post heated X70 steel weldments with a specific geometry The study included experimental and simulation components In the simulation phase, a self restraint cold cracking sensitivity test was modeled according to ISO17642 2 standard The heat transfer problem during the welding process was solved and the residual stresses were calculated throughout the model Hydrogen diffusion and its distribution in steel weldments were also simulated through finite element method In the experimental phase, the hydrogen content of cellulosic and low hydrogen electrodes was measured using the mercury displacement method based on ISO3690 standard The simulation results were validated Thermal validation was conducted by comparing the real and simulated weld pool dimensions, while mechanical validation was achieved by matching simulated residual stresses with measurements obtained through X ray diffraction The plastic strain and local hydrogen concentration resulted from the mechanical and diffusion simulations, respectively Comparing them with the experimental results, a relationship between plastic strain and hydrogen concentration was developed, expressing the amount of critical hydrogen concentration for a given plastic strain in X70 steel to determine the safe area without hydrogen induced cracking Hydrogen induced cracking will not occur if hydrogen concentration is less than this critical amount
کلیدواژهها
نویسندگان
Ali Talebi Hanzaei
Ph D , Department of Materials and Metallurgical Engineering, Amirkabir University of Technology, Tehran, Iran
Emad Cheraghi Rizi
Research Assistant, Department of Materials and Metallurgical Engineering, Amirkabir University of Technology, Tehran, Iran
Seyed Pirooz Hoveida Marashi
Associate Professor, Department of Materials and Metallurgical Engineering, Amirkabir University of Technology, Tehran, Iran
Eslam Ranjbarnodeh
Associate Professor, Department of Materials and Metallurgical Engineering, Amirkabir University of Technology, Tehran, Iran
شیوه ارجاع
Talebi Hanzaei, Ali and Cheraghi Rizi, Emad and Hoveida Marashi, Seyed Pirooz and Ranjbarnodeh, Eslam,1403,Numerical Evaluation of Hydrogen-induced Cracking Susceptibility in X70 Steel Welds Using Finite-element Method,7th International Conference on Welding and Non Destructive Testing & 25th National Conference on Welding & Inspection & 14th National Conference on NDT & 3nd National Conference on Additive Manufacturing,Tehran
ارائهشده در
مجموعه مقالات هفتمین کنفرانس بین المللی جوشکاری وغیرمخرب، بیست و پنجمین کنفرانس ملی جوش و بازرسی، چهاردهمین کنفرانس ملی آزمایش های غیرمخرب و سومین کنفرانس ملی ساخت افزایشی1 اسفند 1403 · تهران